We use cookies to ensure that we give you the best experience on our website. If you click 'Accept all cookies' we'll assume that you are happy to receive all cookies and you won't see this message again. If you click 'Reject all non-essential cookies' only necessary cookies providing core functionality such as security, network management, and accessibility will be enabled. Click 'Find out more' for information on how to change your cookie settings.

© 2017 The Royal Society of Chemistry. Fabrication of oxide thin film transistor (TFT) arrays by inkjet printing with small spacing was investigated, aiming at printing high resolution display backplanes. Two processes are involved during the printing and drying of oxide ink drops; the initial ink drop spreads to a large size upon landing on a substrate and then shrinks to a small size after the solvent dries out. The spreading of the ink drop determines how close two ink drops can be placed and the shrinkage of the ink drop after drying determines the final thickness of the printed dot. It was found that by hydrophobic treatment of the substrate surface with hexamethyldisilazane (HMDS) and octadecyltrichlorosilane (OTS) assembly, the minimum spacing (center-to-center distance) of the printed oxide dot array was reduced from over 80 μm to 45 μm (HMDS treated) and 35 μm (OTS treated), while the dot diameters simultaneously decreased from 70 μm to 20 μm (HMDS treated) and 15 μm (OTS treated). However, too much shrinking caused random movement of the ink drops and an increase of oxide layer thickness, both of which are detrimental to the performance of printed TFTs. To overcome these problems, the ink viscosity was adjusted by adding polyvinylpyrrolidone (PVP) to the ink. With the increase of ink viscosity, the random movement of the ink drops was suppressed and the smallest spacing of 50 μm was achieved for printed oxide TFT arrays. Printed IGZO-TFTs annealed at 350 °C exhibited the highest mobility of about 6.2 cm2 V-1 s-1 and on-to-off current ratio of more than 107.

Original publication




Journal article


Journal of Materials Chemistry C

Publication Date





7495 - 7503