We use cookies to ensure that we give you the best experience on our website. If you click 'Accept all cookies' we'll assume that you are happy to receive all cookies and you won't see this message again. If you click 'Reject all non-essential cookies' only necessary cookies providing core functionality such as security, network management, and accessibility will be enabled. Click 'Find out more' for information on how to change your cookie settings.

Collagen type-II is the dominant type of collagen in articular cartilage and chondroitin sulfate is one of the main components of cartilage extracellular matrix. Afibrillar and fibrillar type-II atelocollagen scaffolds with and without chondroitin sulfate were prepared using casting and freeze-drying methods. The scaffolds were characterised to highlight the effects of fibrillogenesis and chondroitin sulfate addition on viscosity, pore structure, porosity and mechanical properties. Microstructure analysis showed that fibrillogenesis increased the circularity of pores significantly in collagen-only scaffolds, whereas with it, no significant change was observed in chondroitin sulfate- containing scaffolds. Addition of chondroitin sulfate to afibrillar scaffolds increased the circularity of the pores and the proportion of pores between 50 and 300 lm suitable for chondrocytes growth. Fourier transform infrared spectroscopy explained the bonding between chondroitin sulfate and afibrillar collagen- confirmed with rheology resultswhich increased the compressive modulus 10-fold to 0.28 kPa. No bonding was observed in other scaffolds and consequently no significant changes in compressive modulus were detected. © Springer Science+Business Media New York 2013.

Original publication




Journal article


Journal of Materials Science: Materials in Medicine

Publication Date





1153 - 1165